What Is Ductility Test of Bitumen?
The ductility test on bitumen is one of the main tests you need to do when building the road. It helps determine the ductility value of bitumen.
We know that the ductility of a material is the ability of that material to undergo plastic deformation (permanent deformation) before the rupture of that material.
The ductility of a bituminous material is measured by the distance in cm that it elongates before breaking when a standard briquette sample of the material is separated at a specified speed and temperature.
Bitumen ductility measurement test and its suitability for road construction
Understanding what is ductility of bitumen is crucial. Bitumen ductility is expressed as the distance in centimeters by which a standard bitumen briquette can be stretched before the line breaks, this test should be performed at 27 oC and traction should be applied at a rate of 50 mm per minute.
The minimum width of the cross-section of the mold must be 10 mm x 10 mm.
Ductility Bitumen Test
The ductility test of bitumen procedure is crucial. The bitumen ductility test is used to measure the following:
- The ductility of a given bitumen sample is measured
- The suitability of the bitumen for use in road construction is measured.
- Ductility of bitumen is the distance by which it extends in cm before breaking when kept in standard briquettes under standard conditions.
- The standard temperature of 25oC must be maintained. The 100 mm x 100 mm cross-section in the mold is prepared at a specified temperature, the excess bitumen is removed and the chips are hooked after zeroing the pointer.
- The sample is pulled at 50 mm per minute until rupture. The distance to the breaking point in cm is the ductility value that depends on the temperature, briquette size, traction rate.
- Ductility values can vary from 5 to 100 cm. A minimum value of 5 cm is required for bitumen grade 45 and above.
Bitumen Ductility Testing Equipment
Essentially, the following equipment is needed:
Briquettes of Standard Dimensions.
Traction devices with distance measurement display.
Water bath arrangement.
Ductility Bitumen Test Procedure
The bitumen sample is heated to bring it to a liquid state and poured into the set of briquettes and placed on a brass plate.
- All equipment, including bitumen briquette and brass plate, is air-cooled.
- A hot knife is used to cut excess bitumen and the surface is also leveled with the help of a hot knife.
- The whole set is now kept in a bath maintained at 27 oC for about 85 to 95 minutes.
- The mold side has been removed, the clamps hooked on the machine and the pointer set to zero or the initial reading noted.
- The clips are now separated horizontally at a rate of 50 mm per minute and the distance to the point where the line breaks are observed. This distance in cms gives the bitumen ductility value.
- The ductility of the bitumen can vary from 5 to more than 100 for different degrees of bitumen, but, for satisfactory performance, it should not be less than 50.
- The ductility of the bitumen depends on the casting temperature, briquette dimensions, test temperature, tensile rate, etc.
Ductility of the Suitability of Bitumen for Road Construction
Understanding the significance of ductility test of bitumen is essential. For the purpose of flexible pavement design, it is necessary for the binders to form a thin ductile film around the aggregates in order to improve the physical interlocking of the aggregates.
It is important to consider that the binder material with insufficient ductility breaks when subjected to repeated traffic loads and provides a permeable surface of the pavement. In cold weather, bitumen with a low ductility value can crack.
How to Test Ductility Bitumen?
- For many decades, different ductility methods, including the ductility test of bitumen pdf references, have proven to be a reliable indicator of the rheological characteristics of bitumen and bituminous binders at medium temperatures.
- The basic principle of the test is that a bitumen sample is prepared in special molds between two clips. The sample is then separated horizontally at a uniform speed and at a specified temperature in a long water bath.
- Ductility is used as a performance-based specification criterion for bitumen in product specification standards.
Typical Specifications for Standardized Materials That Require a Ductility Test Are:
- Bitumen for paving
- Degree of hard paving and industrial bitumen
- Polymer modified bitumen (PMB)
- Oxidized bitumen
- Asphalt rubber paste
- Chemically modified asphalt cement
- Modified asphalt paste from Lake Trinidad
- Emulsified asphalt
- Bituminous cationic emulsion
- Cut and cast bituminous binders
These ductility tests are carried out in the bitumen refineries laboratory, modified bitumen mixing plants, control laboratories for road construction companies, technical universities (asphalt technology), plants for wall and roof insulation materials, government control and independent road control laboratories.
Three Different Methods of Ductility Testing Are Used in Practice.
Stretching Test
The bitumen is cast in a brass mold. The briquette is then separated in a water bath at a set temperature until it breaks.
The breaking distance indicates the cohesion and general tensile properties of the material. The maximum traction length for highly cohesive material is up to 150 cm.
Standardized tests acc. according to ASTM D 113, DIN 52 013, JIS K 2207 and AASHTO T51 are almost identical. The main test conditions are a traction speed of 5 cm/min and a temperature of 25 ° C in the water bath.
Elastic Recovery Test
Elastic recovery is measured by the recoverable deformation determined after a specified time after cutting an elongated briquette sample.
The sample is pulled to a specified distance and cut with scissors in the middle. After a fixed period of recovery time, the reduction in distance from the total distance is measured.
The test is useful to confirm that a component has been added to the bitumen to provide a significant elastomeric characteristic.
To determine the particular properties of polymer-modified bitumen (PMB), the elastic recovery method proved to be more convenient than the elongation test.
Typical test conditions are a traction speed of 5 cm/min and a temperature of 25 ° C in the water bath.
Test conditions acc. according to ASTM D6084, specify a traction distance of 10 cm and a recovery time of 60 min.
Test conditions acc. according to EN 13 398, specify a traction distance of 20 cm and a recovery time of 30 min.
Ductility Strength Test
The tensile properties are measured based on the executed force and the sample tension until the briquette breaks or a specified tension is reached.
Deformation energy is another significant feature of cohesive power, especially for polymer-modified bitumen.
The energy is determined from the records of the traction curves, calculating the area under the curve. Typical is the area between 20 and 40 cm in traction length. The related standards are EN 13589, EN 13703 and AASHTO T300.
Typical codnitions are a test pull speed of 5 cm/min and a temperature of 4 ° C. according to the AASHTO – US standard and 5 ° C second. for EN standard tests.
Frequently Asked Questions (FAQ) About Ductility Testing of Bitumen
What is the ductility test of bitumen, and why is it important in road construction?
The ductility test measures the ability of bitumen to stretch before breaking. It’s crucial for road construction as it indicates the material’s ability to withstand deformation under traffic loads and resist cracking in cold weather.
How is the ductility of bitumen measured?
Bitumen ductility is measured by the distance in centimeters that a standard briquette can stretch before breaking. This test is conducted at a specified temperature and traction speed.
What equipment is needed for conducting a ductility test?
The equipment includes standard briquettes, traction devices with distance measurement displays, and a water bath arrangement to maintain the specified temperature.
What is the procedure for conducting a ductility test on bitumen?
The bitumen sample is heated and poured into briquette molds, then cooled to a specified temperature. Excess bitumen is removed, and the sample is placed in a water bath. Traction is applied at a constant speed until the sample breaks, and the distance is measured.
What are the typical specifications that require a ductility test?
Bitumen for paving, industrial bitumen, polymer-modified bitumen (PMB), oxidized bitumen, asphalt rubber paste, and various other bituminous binders typically undergo ductility testing.
Are there different methods of ductility testing?
Yes, there are three main methods: stretching test, elastic recovery test, and ductility strength test. Each method assesses different aspects of bitumen’s ductile properties.
How do ductility test results influence the selection of bitumen for road construction?
Ductility test results help in selecting bitumen grades suitable for specific road construction applications. Higher ductility values indicate better flexibility and resistance to cracking, particularly in harsh weather conditions.
What are some common standards used for conducting ductility tests?
Standards such as ASTM D113, DIN 52013, JIS K 2207, AASHTO T51, ASTM D6084, EN 13398, and EN 13703 provide guidelines for conducting ductility tests and interpreting the results.
Can ductility testing identify specific additives in bitumen, such as polymers?
Yes, the elastic recovery method is particularly useful for identifying elastomeric characteristics in bitumen, such as those provided by polymer additives.
What are the implications of ductility test results for pavement design and performance?
Ductility test results influence pavement design by ensuring that binders form a thin, ductile film around aggregates, enhancing pavement durability and performance under varying traffic and weather conditions.